KLEIBERIT 782 GL EVA Hotmelt Adhesive SUPRAMELT CARTRIDGE IVORY COLOR

Description

The smooth thing ... a hot melt cartridge with easy slide coating, KLEIBERIT 782 Supramelt Ivory Color.
Enable Ginger
Cannot connect to Ginger
Check your internet connection
or reload the browser
Disable in this text field
Rephrase
Rephrase current sentence
Edit in Ginger
×
Advantages of the easy slide coating: • Protected from dust The cartridge is protected from contamination, dust and dirt whilst being stored at the work place. In addition to this, even if stored in a warm environment, the cartridges do not stick together. • Problem free melting The new foil coating acts like a lubricant when in the machine. It aids smooth problem free melt rate and dissolves without trace during the melting process. • Increased melting speed The cartridge with the easy slide coasting ensures increased melting speed, which is required to bond wide edges and long substrates. • Easy change of cartridges When color changes are required, the cartridges can be taken out and used again easily, as the foil protects the cartridge.
FIELD OF APPLICATION Bonding of • Epoxy resin edges • Pre-primered ABS edges • Solid wood edges • Polyester edges • Pre-primered PVC-edges • Veneer edges APPLICATION • Both substrates have to be cut to an exact right angle and must be free from dust. • Bring the substrate and the edging material up to room temperature • The ideal moisture content of the wood is 8-10%, room temperature of min. 18 °C, avoid drafts • Pre heat time 2-5 minutes, application temperature 200-220 °C • Correct temperature settings are especially important when bonding solid wood edges • When bonding long and/or ridged pieces the application temperature should be in the higher temperature areas. • Lower temperatures reduce the „wetting out” of the edges • Coat weight and press pressure should be adjusted so that the applied beads are pressed flat, and the adhesives quills out on the edges slightly. To determine the correct coat weight, the use of a transparent edge is advised. NOTE • For solid wood edging the use of linear grain wood is preferable as this is less prone to bend. • To achieve optimum bond strength, the wood grain of the edges should be vertical to the bond surface. • Precisely align the edging material • The chipboard should have a surface which does not have rough cutting marks. • The easy slide coating does not need to be removed prior to processing.
TECHNICAL PROPERTIES • Basis Ethylene-Vinylacetate-Copolymer • Specific gravity approx. 1.3 g/cm³ • Softening point (Ring and Ball) DIN 1995 120 °C ± 10 °C • Melting index DIN 53 735 (MFI 150/2.16) 60 c 15 g/10 min. • Pre heat time 2 - 5 minutes • Speed 8 - 20 m/min., depending on machine